(Summary description)1. When the steel wire is cut off by a sharp object, the end face of the steel wire is broken in an inclined plane along the steel wire; 2. The corroded steel wire is broken through three times of bending and pursing, the end of the fracture is warped, and the end face is rough; the end face is warped, and the end face is rough; 3. Hydrogen embrittlement fracture is mainly caused by long pickling time or long-term immersion in alkaline condition. Hydrogen embrittlement fracture surface and steel wire axis are sharp and rough; 4. The main reason for the formation of martensite structure and fracture surface is that Tianli steel wire rope is impacted and attached at a certain moment during operation; 5. The erosion fatigue fracture has the characteristics of erosion and destruction at the tip, which is cone-shaped and has the characteristics of normal corrosion at the same time; 6. Wear fatigue fracture, after plastic wear, the steel wire is broken after repeated winding and stretching, and the fracture is saw strip; 7. One part of the fracture is in a positive angle, and all of them are split, but the fracture surface is relatively lubrication;
Various broken wires of stainless steel wire rope
(Summary description)1. When the steel wire is cut off by a sharp object, the end face of the steel wire is broken in an inclined plane along the steel wire;
2. The corroded steel wire is broken through three times of bending and pursing, the end of the fracture is warped, and the end face is rough; the end face is warped, and the end face is rough;
3. Hydrogen embrittlement fracture is mainly caused by long pickling time or long-term immersion in alkaline condition. Hydrogen embrittlement fracture surface and steel wire axis are sharp and rough;
4. The main reason for the formation of martensite structure and fracture surface is that Tianli steel wire rope is impacted and attached at a certain moment during operation;
5. The erosion fatigue fracture has the characteristics of erosion and destruction at the tip, which is cone-shaped and has the characteristics of normal corrosion at the same time;
6. Wear fatigue fracture, after plastic wear, the steel wire is broken after repeated winding and stretching, and the fracture is saw strip;
7. One part of the fracture is in a positive angle, and all of them are split, but the fracture surface is relatively lubrication;
- Categories:News
- Author:
- Origin:
- Time of issue:2020-11-21 22:42
- Views:
1. When the steel wire is cut off by a sharp object, the end face of the steel wire is broken in an inclined plane along the steel wire;
2. The corroded steel wire is broken through three times of bending and pursing, the end of the fracture is warped, and the end face is rough; the end face is warped, and the end face is rough;
3. Hydrogen embrittlement fracture is mainly caused by long pickling time or long-term immersion in alkaline condition. Hydrogen embrittlement fracture surface and steel wire axis are sharp and rough;
4. The main reason for the formation of martensite structure and fracture surface is that Tianli steel wire rope is impacted and attached at a certain moment during operation;
5. The erosion fatigue fracture has the characteristics of erosion and destruction at the tip, which is cone-shaped and has the characteristics of normal corrosion at the same time;
6. Wear fatigue fracture, after plastic wear, the steel wire is broken after repeated winding and stretching, and the fracture is saw strip;
7. One part of the fracture is in a positive angle, and all of them are split, but the fracture surface is relatively lubrication;